Fabrics
MS Fabric
- Fabrics
- Glass fabric base
- RoHS Directive
Overview
This fabric has the enhanced release effect by forming a special resin layer on the surface of G type fabric.
Main applications
• Release sheet at the time of mold making.
• Release sheet when making a melting (side seal) bag.
Operating temperature limit
-180℃ to +260℃
Characteristics
• The releas ability is 10 times compared to G type fabric.
• The releas ability is exhibited particularly for highly viscous materials.
Typical dimensions and properties
| Grade | Product code | Total thickness (mm) | Maximum width (mm) | Mass (g/m2) | Tensile strength (N/cm) | Tear strength (N) | Breakdown voltage (kV) | Volume resistivity (Ω-cm) | Surface resistivity (Ω) | Released strength (N/cm) | ||
|---|---|---|---|---|---|---|---|---|---|---|---|---|
| Warp | Fill | Warp | Fill | |||||||||
| Natural / Plain | MS-033 | 0.075 | 1040 | 135 | 167 | 139 | 9 | 8 | 3.5 | 1015 | 1014 | 0.012 |
| MS-053 | 0.080 | 165 | 140 | 110 | 6 | 5 | 5.1 | 0.021 | ||||
| MS-034 | 0.095 | 140 | 329 | 178 | 36 | 13 | 4.2 | 0.014 | ||||
| MS-056 | 0.125 | 265 | 280 | 270 | 11 | 12 | 4.7 | 0.013 | ||||
| MS-038 | 0.165 | 1000 | 275 | 320 | 310 | 23 | 27 | 3.2 | 0.015 | |||
| Test method | JIS L 1096 (Cut-strip method) | JIS L 1096 (Trapezoid method) | JIS C 2110-1 | JIS K 6911 | ||||||||
【Test method】Tensile strength : JIS L 1096 (Cut-strip method) Tear strength：JIS L 1096（Trapezoidal method） / Breakdown voltage/substrate only：JIS C 2110-1 / Volume resistivity、Surface resistivity：JIS K 6911
*Please consult us separately for the dimensions other than above.
*Values shown in this table represent measurements and do not constitute guaranteed values.